3526 Phenolic cotton cloth laminate tube

Similar NEMA C CE L LE Mechanical and electrical applications

Material introduction

high-strength cloth-reinforced phenolic resin is based upon the thermosetting phenolic resin with high-quality cotton fiber or other fibers or fabrics, added with appropriate amount of abrasion-reduction addictives and finally finished with advanced laminating process.PFC high-strength cloth-reinforced phenolic resin, due to reasonable formulation and unique production process, has excellent mechanical, chemical and physical performance. Compared with the frequently used engineering plastic POM, nylon and Teflon, PFC has excellent compressing strength, hardness, heat distortion temperature, impact resistance and self-lubricating abrasion resistance.For many years, PFC high-strength cloth-reinforced phenolic resin have been used in the production of guide rings, support rings as well as various machinery pad and components such as bushes, thrust plates, bearings for the cylinders of engineering machineries.

Specification Color Density g/cm Tensile strength(Mpa) Compressive strength(Mpa) Hardness HRM Mpa* m/s Coefficient of friction Temp. °C Parallel to the laminated plane Vertical to the laminated plane Dry Oil Lubrication Light yellow to brown/black 1.2-1.4 45 168 256 92 0.23-0.46 0.12-0.14 -40 ~ +130

Temperature grade: B glass (130°C)

 Color: nature /black(graphite)

Diameter: 3-600mm

Length: 1000mm

3526 Phenolic cotton cloth laminate tube